The HA material was derived from extracted deproteinized human teeth with calcination at 850 °C for 3 h. Easy separation of the dentine and enamel matter has been observed at that temperature. The 60% of the matter was dentine and 40% is enamel. These parts were subjected to grinding with a blade grinder for 30 s separately. Following this, resulting samples were then sieved and only dentine based HA particles with a particle size of 106-150 ym were used in this study.
The bioglass compositions were prepared from 45 wt.% Si02, 6 wt.% P205, 24,5 wt.% Na2O, 24,5 wt.% CaO known as 45S5. The compositions were placed in platinum crucible and heated to 1330 °C for 4 h. Subsequently they were poured into water in order to be in granular form. They were milled to a powder type particle in a porcelain ball milled for 24 h [3].

По-украински

Матеріал HA був отриманий від витягнутого deproteinized людські зуби з прожаренням в 850 °C за 3 h. Легке відділення дентину і enamel справи спостерігалося в цій температурі. 60f справа була дентином і 40-й емаллю. Ці частини були піддані помелу з точильником леза для 30 s окремо. Йдучи за цим, результуючі зразки потім просіювали і тільки дентин базував ХА частки з розміром частки 106-150, ym були використані в цьому вивченні.
Композиції біокераміки були готові від 45 wt.i02, 6 wt.205, 24,5 wt.a2O, 24,5 wt.aO, відомий як 45S5. Композиції були розміщені в платиновому суворому випробуванні і гарячі до 1330 °C за 4 h. Згодом вони ллється у воду для того, щоб бути в гранульованому формують. Вони молотилися до порошкової type частки у фарфоровому м'ячі молотив за 24 h [3].